BIS - LIMS (Laboratory Information Management System)

RAMCO RESEARCH AND DEVOLPMENT CENTRE

11A,OKKIYAM,THORAIPAKKAM,OLD MAHAPALIPURAM ROAD, CHENNAI, Chennai, Tamil Nadu, 600097

9441824600 trg@ramcocements.co.in

Scope List

Reset

6 Results

S.No.

Indian Standard No.

Product

Grade / Type / Size / Designation etc.

Exclusion

Testing Charges (Excl. Of Taxes)

Facility Type

Effective Date

Validity Date

Remark

IS 12089 (1987)

Specification for granulated slag for the manufacture portland slag cement

1000 View breakup
-

Clause No.	Exclusion	Testing Charges (Excl. Of Taxes)	Remark
3.2(composition of granulated slag, Manganese Oxide)	-	1000	-
3.2(composition of granulated slag, Magnesium Oxide)	-	10000	-
3.2(composition of granulated slag, Sulphide Sulphur)	-	220000	-
3.4(insoluble residue of dried samples)	-	220000	-
4.5(Moisture Content of Granulated Slag)	-	32000	-

Complete

13 Jan, 2025

13 Jan, 2028

IS 1290 (1973)

Specification for mineral gypsum (Second Revision)

11100 View breakup
-

Clause No.	Exclusion	Testing Charges (Excl. Of Taxes)	Remark
3.2 , Table No. 1 , i)(Free water)	-	1000	-
3.2 , Table No. 1 , iii)(Silica and other insoluble matter)	-	2800	-
3.2 , Table No. 1 , iv)(Iron and aluminium (as oxides))	-	2000	-
3.2 , Table No. 1 , v)(Magnesium oxide (as MgO))	-	1000	-
3.2 , Table No. 1 , vi)(Calcium sulphate (as CaSO4.2H2O))	-	1800	-
3.2 , Table No. 1 , vii)(Chlorides (as NaCl))	-	1500	-
3.3.1(Acidity and Alkalinity)	-	1000	-

Complete

13 Jan, 2025

13 Jan, 2028

IS 3812 (Part 1) (2013)

Pulverized fuel ash - Specification: Part 1 For use as pozzolana in cement, cement mortar and concrete

30800 View breakup
-

Clause No.	Exclusion	Testing Charges (Excl. Of Taxes)	Remark
Cl. 6.1, Table 1 - i(Silicon dioxide (SiO2) plus aluminium oxide (Al2O3) plus ironoxide (Fe2O3) - IS 1727)	-	2000	-
Cl. 6.1, Table 1 - ii(Silicon dioxide (SiO2) - IS 1727)	-	1000	-
Cl. 6.1, Table 1 - iii(Reactive Silica - Annex B)	-	3000	-
Cl. 6.1, Table 1 - iv(Magnesium oxide (MgO) - IS 1727)	-	1000	-
Cl. 6.1, Table 1 - vi( Available alkalis as equivalent sodium oxide (Na2O) - Annex C)	-	1000	-
Cl. 6.1, Table 1 - vii( Total Chlorides - IS 4032)	-	1500	-
Cl. 6.1, Table 1 - viii( Loss on ignition - IS 1727)	-	1000	-
Cl. 6.2(Moisture content of the fly ash when supplied in dry condition - Annex D)	-	1000	-
7.1-Table 2(i)(PHYSICAL REQUIREMENTS-Fineness)	-	2000	-
7.1-Table 2(iii)(PHYSICAL REQUIREMENTS-Average compressive strength)	-	3000	-
7.1-Table 2(iv)(PHYSICAL REQUIREMENTS-Compressive strength at 28 days)	-	3000	-
7.1-Table 2(v)(PHYSICAL REQUIREMENTS-Soundness by autoclave test )	-	2000	-
7.2(Uniformity Requirements)	-	1000	-
5.1, 7.1, table-2, iii(Lime reacitivity)	-	3000	-
5.1, 7.1, table-2, iii(Lime reacitivity)	-	3000	-
Cl. 6.1, Table 1 - v( Total sulphur as sulphur trioxide (SO3) - IS 1727)	-	1800	-
5.1&7.1, table-2 (III)(Lime Reactivity)	-	3000	-
7.1-Table 2(ii)(PHYSICAL REQUIREMENTS-Particles retained on 45 micron IS sieve)	-	2000	-

Complete

13 Jan, 2025

13 Jan, 2028

IS 455 (2015)

Portland slag cement - Specification

36100 View breakup
-

Clause No.	Exclusion	Testing Charges (Excl. Of Taxes)	Remark
7 Table 1 iv c(Compretsive Strenqth 672 ± 4 hr IS 4031(Part 6))	-	3000	-
7 Table 1 iv b(Compretsive Strenqth 168 ± 2 hr IS 4031(Part 6))	-	3000	-
7 Table 1 iv a(Compretsive Strenqth .72 ± 1 hr IS 4031(Part 6))	-	3000	-
7 Table 1 iii b(Setting Time ( by Vicat Apparatus ), Final IS 4031(Part 5))	-	2000	-
7 Table 1 iii a(Setting Time ( by Vicat Apparatus ),Initial IS 4031(Part 5))	-	2000	-
7 Table 1 ii b(Soundness, Autoclave expansion IS 4031(Part 3) )	-	2000	-
7 Table 1 ii a(Soundness, Le-Chate1ier expansion IS 4031(Part 3) )	-	2000	-
7 Table 1 i(Fineness IS 4031(Part 2))	-	2000	-
6 - Table - 1 vii( Alkali content as (Na2O + 0.658 K2O) - Cl 4.11 of IS 4032:1985)	-	2000	-
6 - Table - 1 vi(Chloride content - Cl 4.13 of IS 4032:1985)	-	1500	-
6 - Table - 1 v(Loss on ignition - Cl 6.2 of IS 4032:1985)	-	1000	-
6 - Table - 1 iv(Sulphide sulphur (S) - Cl 6.12 of IS 4032:1985)	-	1800	-
6 - Table - 1 iii(Total Sulphur Content calculated as Sulphuric Anhydride (SO3) - Cl 6.11 of IS 4032:1985)	-	1800	-
6 - Table - 1 ii(Magnesia - Cl 6.8 of IS 4032:1985)	-	1000	-
6 - Table - 1 i(Insoluble residue - Cl 6.9 of IS 4032:1985)	-	1800	-
7 Table 1 iv c(Compretsive Strenqth 672 ± 4 hr IS 4031(Part 6))	-	3000	-
7 Table 1 iv b(Compretsive Strenqth 168 ± 2 hr IS 4031(Part 6))	-	3000	-
7 Table 1 iv a(Compretsive Strenqth .72 ± 1 hr IS 4031(Part 6))	-	3000	-
7 Table 1 iii b(Setting Time ( by Vicat Apparatus ), Final IS 4031(Part 5))	-	2000	-
7 Table 1 iii a(Setting Time ( by Vicat Apparatus ),Initial IS 4031(Part 5))	-	2000	-
7 Table 1 ii b(Soundness, Autoclave expansion IS 4031(Part 3) )	-	2000	-
7 Table 1 ii a(Soundness, Le-Chate1ier expansion IS 4031(Part 3) )	-	2000	-
7 Table 1 i(Fineness IS 4031(Part 2))	-	2000	-
6 - Table - 1 vii( Alkali content as (Na2O + 0.658 K2O) - Cl 4.11 of IS 4032:1985)	-	2000	-
6 - Table - 1 vi(Chloride content - Cl 4.13 of IS 4032:1985)	-	1500	-
6 - Table - 1 v(Loss on ignition - Cl 6.2 of IS 4032:1985)	-	1000	-
6 - Table - 1 iv(Sulphide sulphur (S) - Cl 6.12 of IS 4032:1985)	-	3500	-
6 - Table - 1 iii(Total Sulphur Content calculated as Sulphuric Anhydride (SO3) - Cl 6.11 of IS 4032:1985)	-	1800	-
6 - Table - 1 ii(Magnesia - Cl 6.8 of IS 4032:1985)	-	1000	-
6 - Table - 1 i(Insoluble residue - Cl 6.9 of IS 4032:1985)	-	1800	-
Cl. 7 Table-2(Cl. 7 Table-2 i (Fineness ))	-	2000	-
Cl. 7 Table-2(Cl. 7 Table-2 ii a (Expansion after aeration ))	-	2000	-
Cl. 7 Table-2(Cl. 7 Table-2 ii a (Soundness , Le Chatelier Expansion ))	-	2000	-
Cl. 7 Table-2(Cl. 7 Table-2 ii b (Expansion after aeration ))	-	2000	-
Cl. 7 Table-2(Cl. 7 Table-2 ii b (Soundness , Autoclave Expansion ))	-	2000	-
Cl. 7 Table-2(Cl. 7 Table-2 iii a (Setting time Initial))	-	2000	-
Cl. 7 Table-2(Cl. 7 Table-2 iii b (Setting time Final))	-	2000	-
Cl. 7 Table-2(Cl. 7 Table-2 iv a (Compressive Strength 72±1 hr IS))	-	3000	-
Cl. 7 Table-2(Cl. 7 Table-2 iv b (Compressive Strength 168±2 hr ))	-	3000	-
Cl. 7 Table-2(Cl. 7 Table-2 iv c (Compressive Strength 672±4 hr) )	-	3000	-

Complete

13 Jan, 2025

13 Jan, 2028

Exclusion: Clause 7 Table 1 v (Transverse strength)

IS 1489 (Part 1) (2015)

Portland pozzolana cement - Specification: Part 1 fly Ash Based

35100 View breakup
-

Clause No.	Exclusion	Testing Charges (Excl. Of Taxes)	Remark
7 -Table 2- iv- c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 -Table 2- iv- b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 -Table 2- iv- a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 -Table 2-iii- b(Setting Time Final- 4031 Part 5)	-	2000	-
7 -Table 2- iii- a(Setting Time Initial- 4031 Part 5)	-	2000	-
7 -Table 2- ii- b(Expansion by Autoclave- 4031 Part 3)	-	2000	-
7 -Table 2- ii- a(Expansion by Le Chatelier- 4031 Part 3)	-	2000	-
7 -Table 2- i(Fineness 4031 Part 2)	-	2000	-
6 - Table - 1 vi( Alkali content as (Na2O + 0.658 K2O) - Cl 4.11 of IS 4032:1985)	-	2000	-
6 - Table - 1 v(Chloride content - Cl 4.13 of IS 4032:1985)	-	1500	-
6 - Table - 1 iv(Loss on ignition - Cl 7.1 of IS 4032:1985)	-	1000	-
6 - Table - 1 iii(Total Sulphur Content calculated as Sulphuric Anhydride (SO3) - Cl 7.3 of IS 4032:1985)	-	1800	-
6 - Table - 1 ii(Magnesia - Cl 7.2 of IS 4032:1985)	-	1000	-
6 - Table - 1 i(Insoluble residue - Cl 7.4 of IS 4032:1985)	-	1800	-
6 - Table - 1 vi( Alkali content as (Na2O + 0.658 K2O) - Cl 4.11 of IS 4032:1985)	-	2000	-
6 - Table - 1 v(Chloride content - Cl 4.13 of IS 4032:1985)	-	1500	-
6 - Table - 1 iv(Loss on ignition - Cl 7.1 of IS 4032:1985)	-	1000	-
6 - Table - 1 iii(Total Sulphur Content calculated as Sulphuric Anhydride (SO3) - Cl 7.3 of IS 4032:1985)	-	1800	-
6 - Table - 1 ii(Magnesia - Cl 7.2 of IS 4032:1985)	-	1000	-
6 - Table - 1 i(Insoluble residue - Cl 7.4 of IS 4032:1985)	-	1000	-
7 -Table 2- iv- c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 -Table 2- iv- b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 -Table 2- iv- a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 -Table 2-iii- b(Setting Time Final- 4031 Part 5)	-	3000	-
7 -Table 2- iii- a(Setting Time Initial- 4031 Part 5)	-	2000	-
7 -Table 2- ii- a(Expansion by Le Chatelier- 4031 Part 3)	-	2000	-
7 -Table 2- i(Fineness 4031 Part 2)	-	2000	-
6 - Table - 1 vi( Alkali content as (Na2O + 0.658 K2O) - Cl 4.11 of IS 4032:1985)	-	2000	-
6 - Table - 1 v(Chloride content - Cl 4.13 of IS 4032:1985)	-	1500	-
6 - Table - 1 iv(Loss on ignition - Cl 7.1 of IS 4032:1985)	-	1000	-
6 - Table - 1 iii(Total Sulphur Content calculated as Sulphuric Anhydride (SO3) - Cl 7.3 of IS 4032:1985)	-	1800	-
6 - Table - 1 ii(Magnesia - Cl 7.2 of IS 4032:1985)	-	1000	-
6 - Table - 1 i(Insoluble residue - Cl 7.4 of IS 4032:1985)	-	1500	-
6 - Table - 1 vi( Alkali content as (Na2O + 0.658 K2O) - Cl 4.11 of IS 4032:1985)	-	2000	-
6 - Table - 1 v(Chloride content - Cl 4.13 of IS 4032:1985)	-	1500	-
6 - Table - 1 iii(Total Sulphur Content calculated as Sulphuric Anhydride (SO3) - Cl 7.3 of IS 4032:1985)	-	1800	-
6 - Table - 1 ii(Magnesia - Cl 7.2 of IS 4032:1985)	-	1000	-
6 - Table - 1 i(Insoluble residue - Cl 7.4 of IS 4032:1985)	-	1800	-
7 -Table 2- vi(Drying Shrinkage- IS 4031 Part 10)	-	3000	-
7 -Table 2- vi(Drying Shrinkage- IS 4031 Part 10)	-	3000	-
7 -Table 2- ii- a(Expansion after aeration - 4031 Part 3)	-	2000	-
7 -Table 2- ii- b(Expansion after aeration- 4031 Part 3)	-	2000	-
7 -Table 2- ii- b(Expansion after aeration- 4031 Part 3)	-	2000	-
7 -Table 2- ii- b(Expansion by Autoclave- 4031 Part 3)	-	2000	-
6 - Table - 1 iv(Loss on ignition - Cl 7.1 of IS 4032:1985)	-	1000	-
7 -Table 2- ii- a(Expansion after aeration - 4031 Part 3)	-	2000	-

Complete

13 Jan, 2025

13 Jan, 2028

Exclusion: Clause 7 -Table 2- v (Transverse Strength)

IS 269 (2015)

Ordinary portland cement - Specification (Sixth Revision)

43/53/33

36100 View breakup
-

Clause No.	Exclusion	Testing Charges (Excl. Of Taxes)	Remark
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iii b(Setting Time Final)	-	2000	-
7 Table-3 iii a(Setting Time Initial)	-	2000	-
7 Table-3 ii b(Expansion after aeration)	-	2000	-
7 Table-3 ii b(Expansion by Autoclave)	-	2000	-
7 Table-3 ii a(Expansion after aeration)	-	2000	-
7 Table-3 ii a(Expansion by Le Chatelier)	-	2000	-
7 Table-3 i.(Fineness)	-	2000	-
6.1 Table-2 viii(Alkali content)	-	2000	-
6.1 Table-2 vii(Chloride content)	-	1500	-
6.1 Table-2 vi(Loss on ignition)	-	1000	-
6.1 Table-2 v(Total Sulphur Content calculated as Sulphuric Anhydride)	-	1800	-
6.1 Table-2 iv(Magnesia)	-	1000	-
6.1 Table-2 iii.(Insoluble residue)	-	1800	-
6.1 Table-2 ii.(Ratio of percentage of alumina to that of iron oxide)	-	2000	-
6.1 Table-2 i.(Ratio of percentage of lime to percentage of silica, alumina and iron oxide)	-	2000	-
6 - Table - 1 viii(Alkali content as (Na2O + 0.658 K2O) - Cl 4.11 of IS 4032:1985)	-	2000	-
6 - Table - 1 vii(Chloride content - Cl 4.13 of IS 4032:1985)	-	1500	-
6 - Table - 1 vi(Loss on ignition - Cl 4.2 of IS 4032:1985)	-	1000	-
6 - Table - 1 v(Total Sulphur Content calculated as Sulphuric Anhydride (SO3) - Cl 4.9 of IS 4032:1985)	-	1800	-
6 - Table - 1 iv(Magnesia - Cl 4.8 of IS 4032:1985)	-	1000	-
6 - Table - 1 iii(Insoluble residue - Cl 4.10 of IS 4032:1985)	-	1800	-
6 - Table - 1 ii(Ratio of percentage of alumina to that of iron oxide - Cl 4 of IS 4032:1985)	-	2000	-
6 - Table - 1 i(Ratio of percentage of lime to percentages of silica, alumina and iron oxide - Cl 4 of IS 4032:1985)	-	2000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iii b(Setting Time Final)	-	2000	-
7 Table-3 iii a(Setting Time Initial)	-	2000	-
7 Table-3 ii b(Expansion after aeration)	-	2000	-
7 Table-3 ii b(Expansion by Autoclave)	-	2000	-
7 Table-3 ii a(Expansion after aeration)	-	2000	-
7 Table-3 ii a(Expansion by Le Chatelier)	-	2000	-
7 Table-3 i.(Fineness)	-	2000	-
6.1 Table-2 viii(Alkali content)	-	2000	-
6.1 Table-2 vii(Chloride content)	-	1500	-
6.1 Table-2 vi(Loss on ignition)	-	1000	-
6.1 Table-2 v(Total Sulphur Content calculated as Sulphuric Anhydride)	-	1800	-
6.1 Table-2 iv(Magnesia)	-	1000	-
6.1 Table-2 iii.(Insoluble residue)	-	1800	-
6.1 Table-2 ii.(Ratio of percentage of alumina to that of iron oxide)	-	2000	-
6.1 Table-2 i.(Ratio of percentage of lime to percentage of silica, alumina and iron oxide)	-	2000	-
6 - Table - 1 viii( Alkali content as (Na2O + 0.658 K2O) - Cl 4.11 of IS 4032:1985)	-	2000	-
6 - Table - 1 vii(Chloride content - Cl 4.13 of IS 4032:1985)	-	1500	-
6 - Table - 1 vi(Loss on ignition - Cl 4.2 of IS 4032:1985)	-	1000	-
6 - Table - 1 v(Total Sulphur Content calculated as Sulphuric Anhydride (SO3) - Cl 4.9 of IS 4032:1985)	-	1800	-
6 - Table - 1 iv(Magnesia - Cl 4.8 of IS 4032:1985)	-	1000	-
6 - Table - 1 iii(Insoluble residue - Cl 4.10 of IS 4032:1985)	-	1500	-
6 - Table - 1 ii(Ratio of percentage of alumina to that of iron oxide - Cl 4 of IS 4032:1985)	-	2000	-
6 - Table - 1 i(Ratio of percentage of lime to percentages of silica, alumina and iron oxide - Cl 4 of IS 4032:1985)	-	2000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iii b(Setting Time Final)	-	2000	-
7 Table-3 iii a(Setting Time Initial)	-	2000	-
7 Table-3 ii b(Expansion after aeration)	-	2000	-
7 Table-3 ii b(Expansion by Autoclave)	-	2000	-
7 Table-3 ii a(Expansion after aeration)	-	2000	-
7 Table-3 ii a(Expansion by Le Chatelier)	-	2000	-
7 Table-3 i.(Fineness)	-	2000	-
6.1 Table-2 viii(Alkali content)	-	2000	-
6.1 Table-2 vii(Chloride content)	-	1500	-
6.1 Table-2 vi(Loss on ignition)	-	1000	-
6.1 Table-2 v(Total Sulphur Content calculated as Sulphuric Anhydride)	-	1800	-
6.1 Table-2 iv(Magnesia)	-	1000	-
6.1 Table-2 iii.(Insoluble residue)	-	1800	-
6.1 Table-2 ii.(Ratio of percentage of alumina to that of iron oxide)	-	2000	-
6.1 Table-2 i.(Ratio of percentage of lime to percentage of silica, alumina and iron oxide)	-	2000	-
6.1 Table-2 i.(Ratio of percentage of lime to percentage of silica, alumina and iron oxide)	-	2000	-
6.1 Table-2 ii.(Ratio of percentage of alumina to that of iron oxide)	-	2000	-
6.1 Table-2 iii.(Insoluble residue)	-	1800	-
6.1 Table-2 iv(Magnesia)	-	1000	-
6.1 Table-2 v(Total Sulphur Content calculated as Sulphuric Anhydride)	-	1800	-
6.1 Table-2 vi(Loss on ignition)	-	1000	-
6.1 Table-2 vii(Chloride content)	-	1500	-
7 Table-3 i.(Fineness)	-	2000	-
7 Table-3 ii a(Expansion by Le Chatelier)	-	2000	-
7 Table-3 ii a(Expansion after aeration)	-	2000	-
7 Table-3 ii b(Expansion by Autoclave)	-	2000	-
7 Table-3 ii b(Expansion after aeration)	-	2000	-
7 Table-3 iii a(Setting Time Initial)	-	2000	-
7 Table-3 iii b(Setting Time Final)	-	2000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv a(Compressive Strength At 72 hrs ± 1 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv b(Compressive Strength At 168 hrs ± 2 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-
7 Table-3 iv c(Compressive Strength At 672 hrs ± 4 hr - IS 4031 Part 6)	-	3000	-

Complete

13 Jan, 2025

13 Jan, 2028

Exclusion: Clause 7 Table 3, SI No. (v) (Transverse Strength)

Bureau of Indian Standards

The National Standards Body of India

RAMCO RESEARCH AND DEVOLPMENT CENTRE

11A,OKKIYAM,THORAIPAKKAM,OLD MAHAPALIPURAM ROAD, CHENNAI, Chennai, Tamil Nadu, 600097

9441824600 trg@ramcocements.co.in

Scope List