1 |
IS 4985 (2021) |
UNPLASTICIZED PVC PIPES FOR POTABLE WATER SUPPLIES SPECIFICATION Fourth Revision |
-
|
31025.00 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
7(DIMENSIONS-PIPE-Nominal Diameter) |
- |
0 |
|
- |
7.1.1.1(DIMENSIONS-PIPE-Mean O.D. (Minimum)) |
- |
0 |
|
- |
7.1.1.1(DIMENSIONS-PIPE-Mean O.D. (Mamimum)) |
- |
0 |
|
- |
7.1.1.1(DIMENSIONS-PIPE-Mean O.D. Variation) |
- |
0 |
|
- |
7.1.2.1(DIMENSIONS-PIPE-Thickness(Minimum)) |
- |
0 |
|
- |
7.1.2.1(DIMENSIONS-PIPE-Thickness(Maximum)) |
- |
0 |
|
- |
7.1.2.1(DIMENSIONS-PIPE-Average Thickness) |
- |
500 |
|
All dimensions are included in this mentioned test charge |
7.2.1.1-Table 3(DIMENSIONS-Socket-Sockets for solvent cement jointing-Minimum Length) |
- |
0 |
|
- |
7.2.1.1-Table 3(DIMENSIONS-Socket-Sockets for solvent cement jointing-Diameter at mid point of the socket length (Minimum)) |
- |
0 |
|
- |
7.2.1.1-Table 3(DIMENSIONS-Socket-Sockets for solvent cement jointing-Diameter at mid point of the socket length (Maximum)) |
- |
0 |
|
- |
7.2.1.2(a)-Table 5(DIMENSIONS-Sockets for elastomeric sealing ring joints-Minimum depth of engagement) |
- |
0 |
|
- |
10.1.1(PHYSICAL AND CHEMICAL CHARACTERISTICS-Visual Appearance) |
- |
300 |
|
- |
10.2(PHYSICAL AND CHEMICAL CHARACTERISTICS-Opacity) |
- |
575 |
|
- |
10.4(PHYSICAL AND CHEMICAL CHARACTERISTICS- Reversion Test) |
- |
900 |
|
- |
9.1(PIPE ENDS) |
- |
0 |
|
- |
10.5(PHYSICAL AND CHEMICAL CHARACTERISTICS- Vicat Softening Temperature) |
- |
1100 |
|
- |
10.6(PHYSICAL AND CHEMICAL CHARACTERISTICS- Density) |
- |
500 |
|
- |
11.1-Table 6(MECHANICAL PROPERTIES-Hydrostatic Pressure Test (Type Test)) |
- |
11000 |
|
- |
11.1-Table 6(MECHANICAL PROPERTIES-Hydrostatic Pressure Test (Acceptance Test)) |
- |
8501 |
|
- |
11.1-Table 7(MECHANICAL PROPERTIES-Hydrostatic Pressure Test (Type Test)-for Integral Sealing Ring Sockets) |
- |
5000 |
|
- |
11.1.1(MECHANICAL PROPERTIES-Hydrostatic Pressure Test (Acceptance Test)-for Plumbing pipes) |
- |
850 |
|
- |
10.7(Sulphated Ash Content) |
- |
950 |
|
- |
11.2(Resistance to External Blows at 0°C) |
- |
1400 |
|
- |
10.3(Effect on Water Test) |
- |
3000 |
|
- |
6.1.2(PVC Resin) |
- |
4100 |
|
K Value & VCM content are included in the mentioned test charge |
|
Complete
|
|
31 Dec, 2023 |
- |
2 |
IS 16208 (2015) |
Textiles - High density polyethylene (HDPE)/polypropylene (PP) woven sacks for packaging 10 kg, 15 kg, 20 kg, 25 kg and 30 kg foodgrains - Specification |
-
|
19480 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
4.1(Raw Material) |
- |
1050 |
|
- |
4.2(Tapes – Width
IS 6192 and IS 11197) |
- |
250 |
|
- |
4.3(Sacks) |
- |
300 |
|
- |
4.3.1( The two rows of stitches shall be separated from each other) |
- |
0 |
|
- |
4.4 and Table 1 i(Capacity) |
- |
250 |
|
- |
5.2 and Table 1 ii a(Dimensions Inside Length) |
- |
250 |
|
- |
5.2 and Table 1 ii b(Dimensions Inside Width) |
- |
0 |
|
- |
5.2 and Table 1 iii(Ends per dm ) |
- |
250 |
|
- |
5.2 and Table 1 iv(Picks per dm ) |
- |
250 |
|
- |
5.1 and Table 1 v(Mass of sack ) |
- |
250 |
|
- |
5.2 and Table 1 vi a(Average breaking strength of fabric Lengthwise ) |
- |
2200 |
|
- |
5.2 and Table 1 vi b(Average breaking strength of fabric Widthwise ) |
- |
0 |
|
- |
5.2 and Table 1 vi(Breaking strength of bottom seam ) |
- |
1100 |
|
- |
5.2 and Table 1 viii a(Elongation at break of fabric Lengthwise) |
- |
0 |
|
- |
5.2 and Table 1 viii b(Elongation at break of fabric Widthwise ) |
- |
0 |
|
- |
5.2 and Table 1 ix(Average breaking strength and elongation at break of UV stabilized HDPE/PP fabric after been exposed to UV radiation and weathering ) |
- |
11130 |
|
- |
5.2 and Table 1 x(Ash content ) |
- |
950 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
3 |
IS 15801 (2008) |
Polypropylene - Random copolymer pipes for hot and cold water supplies - Specification |
-
|
24380 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
Cl 7(Dimensions Of Pipes) |
- |
250 |
|
- |
Cl 8(Visual Appearance) |
- |
300 |
|
- |
Cl 9.1(Hydraulic Characteristics) |
- |
18400 |
|
- |
Cl 9.2(Fusion Compatibility) |
- |
4800 |
|
- |
Cl 9.3(Reversion Test ) |
- |
1000 |
|
- |
Cl 9.4 & Annex B(Impact Strength) |
- |
1400 |
|
- |
Cl 9.5(Density) |
- |
500 |
|
- |
Cl 9.6(Melt Flow Rate) |
- |
1100 |
|
- |
Cl 9.7(Carbon Black Content & Dispersion) |
- |
1625 |
|
CBC & CBD inclusive |
Cl 9.8(Thermal Stability By Hydrostatic Pressure Testing) |
- |
83825 |
|
- |
Cl 9.9(Opacity) |
- |
575 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
4 |
IS 15778 (2007) |
Chlorinated polyvinyl chloride (Cpvc) pipes for potable hot and cold water distribution supplies - Specification |
-
|
16525 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
6.3(Compound Properties) |
- |
1100 |
|
- |
6.3.1
Annex B(Chloride content) |
- |
8600 |
|
- |
9.1(Visual Appearance) |
- |
550 |
|
- |
9.5
IS 12235(Part 2)(Vicat Softening Temperature:
When tested by the method prescribed in IS 12235(Part 2), the Vicat softening temperature of the specimen
shall not be less than 110°C.) |
- |
1100 |
|
- |
10(Mechanical Properties) |
- |
1725 |
|
- |
10.5
IS 12235(Part 13)(Tensile Strength :
When tested by the method prescribed in IS 12235(Part 13), the tensile strength at yield shall not be less than 50 MPaat 27±2°C.
) |
- |
3450 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
5 |
IS 15609 (2005) |
Polyethylene flexible pouches for the packing of natural mineral water and packaged drinking water - Specification |
-
|
14000 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
6.1.1(Description) |
- |
500 |
|
- |
6.1.2(Film Form) |
- |
0 |
|
- |
6.1.3(Winding of the Film ) |
- |
0 |
|
- |
6.1.4(Odour) |
- |
0 |
|
- |
6.1.5 A-2 of IS: 2508:2016(Thickness) |
- |
250 |
|
- |
6.1.6(Width) |
- |
250 |
|
- |
6.1.7 IS: 9845:1998(Migration- a. Amount of extractive ) |
- |
1700 |
|
- |
6.1.8 Annex 4 of IS:2508:2016(Tensile Strength b. Crosswise direction) |
- |
2200 |
|
- |
6.1.8 Annex 4 of IS:2508:2016(Tensile Strength a. Lengthwise direction) |
- |
0 |
|
- |
6.1.9 Annex 4 of IS:2508:2016(Elongation at break - a. Lengthwise direction) |
- |
0 |
|
- |
6.1.9 Annex 4 of IS:2508:2016(Elongation at break - b. Crosswise direction) |
- |
0 |
|
- |
6.1.10 Annex -6 of IS:2508:2016(Dart impact Resistance) |
- |
850 |
|
- |
Cl. 7.1(Vibration Leakage Test) |
- |
1000 |
|
- |
7.1 Annex E(Water Potability test (after 30 Days) a) Taste b) Odour) |
- |
2900 |
|
- |
7.2 Annex F(Stack Load test) |
- |
900 |
|
- |
7.3 Annex G(Drop test ) |
- |
1100 |
|
- |
7.4 Annex H(Ink adhesion test for printed pouches) |
- |
500 |
|
- |
7.5 Annex J(Product resistance test for printed pouches) |
- |
500 |
|
- |
5(Material) |
- |
1350 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
6 |
IS 15410 (2003) |
Containers for packaging of natural mineral water and packaged drinking water - Specification |
-
|
7000 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
4.0 (chem)(MATERIAL) |
- |
1050 |
|
- |
4.2 (chem)(Design, Shape & Dimension) |
- |
250 |
|
- |
4.1 (chem)(Workmanship and Finish) |
- |
0.0 |
|
- |
Cl. 4.4 (a) (chem)(Capacity) |
- |
0.0 |
|
- |
4.5 (chem)(a) Wall Thickness, mm Top) |
- |
0.0 |
|
ABOVE ALL TESTS ARE INCLUDED |
4.6.2(TRANSPARANCY) |
- |
700 |
|
- |
4.6.3(LEAKAGE TEST) |
- |
1000 |
|
- |
4.6.4(DROP TEST) |
- |
1100 |
|
- |
4.6.5(MIGRATION TEST) |
- |
2900 |
|
- |
4.6.6(PORTABILITY TEST) |
- |
0.0 |
|
MIGRATION & POTABILITY TEST CHARGES ARE INCLUDED TOGETHER |
|
Complete
|
|
31 Dec, 2023 |
- |
7 |
IS 14968 (2015) |
Textiles – High density polyethylene (HDPE)/ polypropylene (PP) woven sacks for packing 50 Kg/25 kg sugar – Specification (first revision) |
-
|
19630 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
4.1(Raw Material) |
- |
1050 |
|
- |
4.2(Tapes – Width
IS 6192 and IS 11197) |
- |
250 |
|
- |
4.3.1(The two rows of stitches shall be separated from each other) |
- |
300 |
|
- |
4.4(Bottom seam of the loose liner) |
- |
250 |
|
- |
4.5 and Table 1 i(Capacity) |
- |
250 |
|
- |
5.2 and Table 1 ii a(Dimensions Inside Length) |
- |
250 |
|
- |
5.2 and Table 1 ii b(Dimensions Inside Width) |
- |
0 |
|
- |
5.2 and Table 1 iii(Ends per dm ) |
- |
200 |
|
- |
5.2 and Table 1 iv(Picks per dm ) |
- |
200 |
|
- |
5.1 and Table 1 v a(Mass of unlaminated sack
IS 1964) |
- |
250 |
|
- |
5.2 and Table 1 vi a(Average breaking strength of fabric Lengthwise
IS 1969 (Part 1)) |
- |
1100 |
|
- |
5.2 and Table 1 vi b(Average breaking strength of fabric Widthwise
IS 1969 (Part 1)) |
- |
0 |
|
- |
5.2 and Table 1 vi(Breaking strength of bottom seam
IS 9030
) |
- |
1100 |
|
- |
5.2 and Table 1 viii a(Elongation at break of fabric Lengthwise
IS 1969 (Part 1)) |
- |
1100 |
|
- |
5.2 and Table 1 viii b(Elongation at break of fabric Widthwise
IS 1969 (Part 1)) |
- |
0 |
|
- |
5.2 and Table 1 ix(Average breaking strength and elongation at break of UV stabilized HDPE/PP fabric after been exposed to UV radiation and weathering ) |
- |
12380 |
|
- |
5.2 and Table 1 x(Ash content ) |
- |
950 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
8 |
IS 14887 (2014) |
Textiles – High density polyethylene (HDPE)/ polypropylene (PP) woven sacks for packaging of 50 kg food grains – Specification (first revision) |
-
|
18330 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
3.2(Tapes – Width and Thickness
( IS 6192/IS 11197)) |
- |
250.00 |
|
- |
3.2(Tapes – Linear Density
(IS 6192/IS 11197)) |
- |
0.0 |
|
NA |
3.2(Tapes – Tenacity (IS 6192/IS 11197)) |
- |
0.0 |
|
NA |
3.2(Tapes – Elongation at point of rupture
(IS 6192/IS 11197)) |
- |
0.0 |
|
NA |
3.2(Tapes – Heat Shrinkage (HDPE) (Cl. 3.2 and IS 6192)) |
- |
0.0 |
|
NA |
3.2(Tapes – Dimensional stability (PP)
(IS 11197)) |
- |
0.0 |
|
NA |
3.3.1(Bottom seam (IS 10789)) |
- |
250 |
|
- |
4.1 and 3.4(Mass of bale (Cl. 4.1), Capacity (Cl 3.4)) |
- |
250 |
|
- |
4.2 and Table 1 ii(Dimensions ) |
- |
250 |
|
- |
5.2 and Table 1 iii(Ends per dm ) |
- |
200 |
|
- |
5.2 and Table 1 iv(Picks per dm ) |
- |
200 |
|
- |
4.2 and Table 1 v(Mass of sack ) |
- |
300 |
|
- |
4.2 and Table 1 vi(Average breaking strength of fabric ) |
- |
1100 |
|
- |
4.2 and Table 1 vi(Breaking strength of bottom seam ) |
- |
1100 |
|
- |
4.2 and Table 1 viii(Elongation at break of fabric ) |
- |
1100 |
|
- |
4.2 and Table 1 ix(Average breaking strength and elongation at break of UV stabilized HDPE/PP fabric after been exposed to UV radiation and weathering ) |
- |
12380 |
|
- |
4.2 and Table 1 x(Ash content ) |
- |
950 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
9 |
IS 14735 (1999) |
Unplasticized Polyvinyl Chloride (UPVC) Injection Moulded Fittings for Soil and Waste Discharge System for Inside and Outside Buildings Including Ventilation and Rain Water System - |
-
|
11250 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
5(Colour of fittings) |
- |
300 |
|
- |
10(Workmanship) |
- |
300 |
|
- |
7.1,Table 1(Wall thickness) |
- |
0 |
|
- |
7.2 ,Table 2&3(Socket Dimensions) |
- |
500 |
|
- |
12.1(Visual appearance) |
- |
300 |
|
- |
12.2(Stress relief test) |
- |
700 |
|
- |
12.3(Vicat softening tempewrature) |
- |
1100 |
|
- |
Cl.13, IS 12235 (P-7)-2004, (Resistance to Sulphuric Acid) |
- |
2500 |
|
- |
Cl.14, Annex A(Titanium Di-Oxide Content) |
- |
1200 |
|
- |
Cl.15, Annex B(Sulphated Ash Content) |
- |
950 |
|
- |
16.1(Impact test) |
- |
1000 |
|
8950 FOR PRODUCT & 2300 FOR RAW MATERIAL.TOTAL IS 11250 |
|
Complete
|
|
31 Dec, 2023 |
- |
10 |
IS 14333 (1996) |
High Density Polyethylene Pipe For Sewerage - |
-
|
11075 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
6(Dimensions of pipes) |
- |
0 |
|
- |
7(Visual Appearance) |
- |
300 |
|
- |
8.1(Hydraulic characteristics) |
- |
6400 |
|
4800 for type test & 1600 for acceptance test |
4(Colour) |
- |
250 |
|
- |
8.2(Reversion) |
- |
900 |
|
- |
8.3(Density) |
- |
500 |
|
- |
8.4(Melt Flow Rate) |
- |
1100 |
|
- |
Cl. 8.5, IS 2530-1963, Cl. 10(Cabon Black Content) |
- |
925 |
|
- |
Cl. 8.5, IS 2530-1963, Cl. 16(Carbon Black Dispersion) |
- |
700 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
11 |
IS 14252 (2015) |
Textiles – High density polyethylene (HDPE)/ polypropylene (PP) woven sack for filling sand – Specification (second revision) |
-
|
18930 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
3.1(Raw Material) |
- |
1050 |
|
- |
3.2(Tapes – Width
) |
- |
0.0 |
|
- |
3.2(Tapes – Linear Density
) |
- |
0.0 |
|
Attached separately |
3.4(Sack) |
- |
0.0 |
|
- |
3.4.1(Seam) |
- |
0.0 |
|
- |
4.1 and Table 1 i a(Dimensions Outside Length) |
- |
250 |
|
- |
4.1 and Table 1 i b(Dimensions Outside Width) |
- |
250 |
|
- |
4.1 and Table 1 ii(Ends per dm ) |
- |
250 |
|
- |
4.1 and Table 1 iii(Picks per dm ) |
- |
250 |
|
- |
4.2 and Table 1 iv(Mass of sack
) |
- |
250 |
|
- |
4.1 and Table 1 v a(Average breaking strength of fabric Warpway
) |
- |
1100 |
|
- |
4.1 and Table 1 v b(Average breaking strength of fabric Weftway
) |
- |
1100 |
|
Tensile Strength & Elongation charges are inclusive |
4.1 and Table 1 vi(Average Breaking strength of bottom seam ) |
- |
1100 |
|
Tensile Strength & Elongation charges are inclusive |
4.1 and Table 1 vii a(Elongation at break of fabric Lengthwise) |
- |
0.0 |
|
Mentioned above |
4.1 and Table 1 vii b(Elongation at break of fabric Widthwise ) |
- |
0.0 |
|
Mentioned above |
4.1 and Table 1 viii(Average breaking strength and elongation at break of UV stabilized HDPE/PP fabric after been exposed to UV radiation and weathering ) |
- |
2200 |
|
Lengthwise & width wise test charges are inclusive |
4.1 and Table 1 ix(Ash content ) |
- |
950 |
|
- |
3.3(Tying Cord) |
- |
0.0 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
12 |
IS 14182 (1994) |
Solvent cement for use with unplasticized polyvinyl chloride plastic pipe and fittings - Specifications |
-
|
9450 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
4.5(REQUIREMENTS) |
- |
300 |
|
- |
4.5(When used under the conditions for which they are designed, non metallic materials in contact with or likely to come in contact with potable water shall not constitute a toxic hazard , shall not support microbial growth and shall not give rise to unpleasant taste or odour, cloudiness or discolouration of the water) |
- |
3000 |
|
- |
4.8(Dissolution) |
- |
400 |
|
- |
4.9 and 6.1(Viscosity) |
- |
1100 |
|
- |
4.10 and 6.1(Lap Shear Strength - After 2 h curing time) |
- |
0 |
|
- |
4.10 and 6.1(Lap Shear Strength - After 10 h curing time) |
- |
0 |
|
- |
4.10 and 6.1(Lap Shear Strength - After 72 h curing time) |
- |
3800 |
|
- |
4.11 and 6.1(Hydrostatic Burst Strength - After 2 h curing time) |
- |
850 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
13 |
IS 13958 (1994) |
Bamboo Mat Board For General Purposes -specification |
-
|
17375 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
6(Dimensions and tolerances) |
- |
1200 |
|
- |
7.1(Workmanship and finish) |
- |
300 |
|
- |
7.2(Workmanship and finish) |
- |
0 |
|
- |
9.3.1(Internal bond strength in Dry State) |
- |
1350 |
|
- |
9.3.2(Internal bond strength in Wet State) |
- |
1350 |
|
- |
9.4.2(surface strength test in Wet State) |
- |
2025 |
|
- |
9.4.3(Mycological Test) |
- |
7650 |
|
- |
5.2(Application of Adhesive) |
- |
1800 |
|
- |
5.4(Assembly) |
- |
650 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
14 |
IS 13714 (1993) |
Dunnage pallets - Warehousing - Specification |
-
|
3550 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
4.1(DIMENSIONS) |
- |
750 |
|
- |
5.1.2(Timber) |
- |
700 |
|
- |
5.1.2.1 (Objectionable knots) |
- |
300 |
|
- |
6.1.2(CONSTRUCTION) |
- |
1500 |
|
- |
7(WORKMANSHIP AND FINISH) |
- |
300 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
15 |
IS 13592 (2013) |
Unplasticized Polyvinyl Chloride (PVC-U) Pipes for Soil and Waste Discharge System Inside and Outside Buiildings Including Ventilation and Rainwater System |
-
|
17100 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
Cl6.3(The composition shall be based on PVC resin
having a K-value of 64 or greater when tested in
accordance with IS 4669) |
- |
1100 |
|
- |
Cl.5(Surface colour of the pipes shall be dark shade of grey) |
- |
300 |
|
- |
Cl.7.1(Mean outside diameter, outside diameter at any point
for Type A and Type B pipes
manufactured plain or with socket shall be as given in
Table 1. Dimensions shall be measured according to
the method given in IS 12235 (Part 1).) |
- |
500 |
|
- |
Cl.7.1( wall thickness at any point
for Type A and Type B pipes
manufactured plain or with socket shall be as given in
Table 1. Dimensions shall be measured according to
the method given in IS 12235 (Part 1).) |
- |
0.0 |
|
INCLUDED ABOVE |
Cl.8.1(The internal and external surface of the pipes shall be
smooth and clean, and free from grooving and other
defects. The end shall be clearly cut and shall be square
with the axis of the pipe. The end may be chamfered
on the plain side.) |
- |
300 |
|
- |
Cl.8.2(When tested by the method described in IS 12235
(Part 5), a length of pipe sample of 200 ± 20 mm shall
not alter in length by more than 5 percent. In the case
of socket ended pipes, this test shall be carried out on
the plain portion of pipe taken at least 100 mm away
from the root of the socket.) |
- |
1000 |
|
- |
Cl8.3(This test shall be carried out for socket end pipes only.
When tested by the method described in IS 12235
(Part 6), the test specimens shall not show blisters,
excessive delamination or cracking or signs of weld
line splitting.) |
- |
700 |
|
- |
Cl.8.4(When determined in accordance with IS 12235 (Part 2),
the vicat softening temperature of the specimen shall
not be less than 79°C.) |
- |
1100 |
|
- |
Cl.8.5(After the required
period of exposure, the tensile strengths of two samples when tested as per IS 12235 (Part 13) shall not show
difference of more than 20 percent of their initial tensile
strengths) |
- |
4850 |
|
3500+1350 |
Cl. 9, IS 12235 Part 7(Resistance to Sulphuric Acid) |
- |
2500 |
|
- |
Cl.10.1(When tested by method prescribed in IS 12235 (Part 9),the pipe shall have a true impact rate of not more than
10 percent. Mass of striker and height of fall shall be
as per Annex A.) |
- |
1400 |
|
- |
Cl.10.2(When determined in accordance with the method
described in IS 12235 (Part 13), the tensile strength at
break shall not be less than 45 MPa.) |
- |
1350 |
|
- |
Cl.11.(Jointing of solvent
cementing joints is to be carried out using solvent
conforming to IS 14182.
Apply a pressure of 0.05 MPa for a period of 15 min
and there should be no leakage at any joint.) |
- |
1000 |
|
- |
Cl. 12, IS 12235 Part 11(Resistance to Di-Chloro-Methane ) |
- |
1000 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
16 |
IS 12818 (2010) |
Unplasticized polyvinyl chloride (Pvc - U) screen and casing pipes for bore/tubewells - Specification (Second Revision) |
-
|
11725 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
4.1.2(K-Value as per IS-4669) |
- |
1100 |
|
- |
5.0(Colour of Pipes) |
- |
300 |
|
- |
9.1( Visual Appearance) |
- |
0 |
|
colour & visual appearance are inclusive to above charge |
7.1 and Table 1, 2, 3, & 4
Fig 1A & 1B(Nominal Diameter) |
- |
1500 |
|
all |
7.2 and Table 5, 6 & 7
Fig 1B(Wall thickness, Max) |
- |
0 |
|
all dimensions added to above charge |
8.1 to 8.3 and Table 11 &12
Fig 3A & 4A(THREADING OF SCREEN ANDCASING PIPES.
IS 554.) |
- |
250 |
|
- |
8.4(Sealing rings - Hardness) |
- |
375 |
|
- |
9.2(Internal Diameter) |
- |
350 |
|
- |
9.3(Density
IS 12235 (Part 14)) |
- |
500 |
|
- |
9.4 and Table 14(Resistance to External Blows at 0 ?C
IS 12235 (Part 9)) |
- |
1400 |
|
- |
9.5(Tensile Strength
IS 12235(Part 13)) |
- |
1600 |
|
- |
9.6(Vicat Softening Temperature
IS 12235 (Part 2).) |
- |
1100 |
|
- |
9.7(Effect on Water
a) Lead (first extraction)
b) Lead (Third extraction)
c) Dialkyl Tin C4 & higher homologues measured as Tin (Third extraction)
d) Cadmium (All three extracts)
e) Mercury (All three extracts)
f) Other Toxic Substances
) |
- |
3000 |
|
- |
8.4.1 and Table 13
Fig 3B & 4B(Dimensions of sealing elements) |
- |
250 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
17 |
IS 12786 (1989) |
Irrigation equipment - Polyethylene pipes for irrigation laterals - Specification |
-
|
16425 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
4.1.a (Potyethylene - higher olefins constituent ) |
- |
2150 |
|
- |
4.1.c.i (Density) |
- |
1125 |
|
- |
4.1.c.ii (Toluene extract - Annex A) |
- |
1100 |
|
- |
4.1.c.iii (Volatile matter - Annex B ) |
- |
700 |
|
- |
4.1.c & 4.2.a (Carbon Black content - IS 2530 : 1963) |
- |
925 |
|
- |
4.2.b (The dispersion of Carbon Black content shall be satisfactory - IS 2530 : 1963) |
- |
700 |
|
- |
6.1(Visual Appearance) |
- |
300 |
|
- |
5 and Table 1(DIMENSIONS OF PIPES - outside diameters) |
- |
250 |
|
- |
5 and Table 1(DIMENSIONS OF PIPES - wall thickness shall) |
- |
0 |
|
- |
7.2(Reversion Test) |
- |
1000 |
|
- |
7.3(Tensile Test) |
- |
1350 |
|
- |
7.4(SusceptibiIity to Environmental Stress
Cracking) |
- |
1200 |
|
- |
7.1
Table-2
(b)Acceptance Test for 01 hour at 20°C & 6.9MPa induced stress) |
- |
1000 |
|
- |
7.1
Table-2
(Hydraulic Characteristics
a)Quality Test for 100 hours at 70°C & 2.5.MPa induced stress.
) |
- |
3000 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
18 |
IS 12701 (1996) |
Rotational moulded polyethylene water storage tanks - specification (First Revision) |
-
|
18250 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
4.2.3(Carbon Black Content ) |
- |
925 |
|
nil |
4.2.3(Carbon Dispersion Test) |
- |
700 |
|
nil |
5.1 Table 1(Dimensioas of Cylinderical Vertical Tank) |
- |
250 |
|
for net & gross capacity |
5.1 Table 1(Dimensioas of Cylinderical Vertical Tank) |
- |
250 |
|
for over all diameter |
5.1 Table 1(Dimensioas of Cylinderical Vertical Tank) |
- |
250 |
|
for over all height |
5.1 Table 1(Dimensioas of Cylinderical Vertical Tank) |
- |
250 |
|
for internal dia of man hole |
5.2 Table 2(Dimensions of Rectangular Loft Tanks) |
- |
500 |
|
for net & gross capacity |
5.2 Table 2(Dimensions of Rectangular Loft Tanks) |
- |
250 |
|
for overall diameter |
5.2 Table 2(Dimensions of Rectangular Loft Tanks) |
- |
250 |
|
for overall height |
5.2 Table 2(Dimensions of Rectangular Loft Tanks) |
- |
250 |
|
for internal dia of manhole |
7.1.1(Resistance to Deformation) |
- |
700 |
|
nil |
7.1.2(Resistance to Deformation) |
- |
700 |
|
nil |
7.2(Resistance to Impact) |
- |
1100 |
|
nil |
7.3(Test for Top Load Resistance) |
- |
1100 |
|
nil |
7.4(Tensile Strength) |
- |
1350 |
|
nil |
7.5(Flexural Modulus) |
- |
1350 |
|
nil |
7.6(overall Migration) |
- |
2200 |
|
nil |
9.2.1(Man-Hole and Hand-Hole Lids) |
- |
200 |
|
- |
9.1(Man-Hole and Hand-Hole Lids) |
- |
3225 |
|
- |
5.4(Wall Thickness above effective height) |
- |
250 |
|
- |
5.2 Table 2 (7)(Minimum Wall Thickness) |
- |
250 |
|
- |
5.1 Table 1 (7)(Minimum Weight of Tank (Without Lid)) |
- |
500 |
|
- |
5.1 Table 1(Dimensioas of Cylinderical Vertical Tank) |
- |
250 |
|
Gross Capacity |
5.1 Table 1(Dimensioas of Cylinderical Vertical Tank) |
- |
250 |
|
Internal Manhole |
5.3(Types and Features ) |
- |
0 |
|
Visual Inspection of Flat area |
5.6(Types and Features ) |
- |
0 |
|
- |
9.1(Lid Thickness) |
- |
0 |
|
- |
6.1(Finish) |
- |
0 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
19 |
IS 11652 (2017) |
Textiles – High density polyethylene (HDPE)/ polypropylene (PP) woven sacks for packaging of 50 kg cement – Specification (third revision) |
-
|
25330 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
4.1(Raw Material
) |
- |
1050 |
|
- |
4.2
(Fabric) |
- |
250 |
|
- |
4.3(Sacks) |
- |
300 |
|
- |
4.4(Seam
) |
- |
0 |
|
- |
4.4(The material used for stitching shall be HDPE/PP tape having minimum 20 percent higher denier than the tapes used
in the fabric.) |
- |
1050 |
|
- |
4.4(Seam) |
- |
250 |
|
- |
4.2
(The
denier of HDPE/ PP tape used in the manufacture of
woven fabric shall be subjected to the
tolerances: a) ± 10 percent on individual value, and
) |
- |
500 |
|
- |
4.5(Lamination ) |
- |
1250 |
|
- |
4.6(Capacity The sack shall have the nominal filling capacity of 50 kg) |
- |
400 |
|
- |
4.7(and then stitching shall be done through six layers.) |
- |
250 |
|
- |
Fig. 1- Table 1- Sr. no. i
(Dimensions, mm (see Note )- Annex B
c) Width of gusset (e) 76 ± 10 mm
) |
- |
1150 |
|
MASS & DIMENSIONS CHARGE ARE INCLUSIVE |
Fig. 1- Table 1-Sr. no. iii
(Picks per dm-Annex B 40 ± 2 ) |
- |
0 |
|
- |
5/5.3-Table 1-Sr. no.v(Average breaking strength of fabric [Ravelled strip method, 325 mm × 70 mm] Min, N(kgf): -1969 (Part 1) a) Lengthwise , 900 (91.8) ) |
- |
1100 |
|
- |
5/5.3-Table 1-Sr. no.v(Average breaking strength of fabric [Ravelled strip method, 325 mm × 70 mm] Min, N(kgf): - 1969 (Part 1) b) Widthwise , 900 (91.8) ) |
- |
1100 |
|
- |
5/5.3-Table 1-Sr. no.vi(Breaking strength of top seam (Ravelled strip method), Min, - IS 9030 N (kgf) 400 (40.8)) |
- |
1100 |
|
- |
5/5.3-Table 1-Sr. no.vi(Breaking strength of bottom seam (Ravelled strip method), Min, - IS 9030 N (kgf) 400 (40.8)) |
- |
1100 |
|
- |
5/5.4-Table 1-Sr. no.viii(Drop impact strength - Annex C No failure) |
- |
1100 |
|
- |
5/5.5-Table 1-Sr. no.viii(Ash content Max percent- Annex D a) For UV stabilized sacks 2.2
) |
- |
950 |
|
- |
5/5.6 (UV Resistance, ) |
- |
10180 |
|
- |
5/5.6 (UV Resistance, The UV stabilized woven fabric shall have at least 50 percent retention of the original breaking strength when tested after the same has been exposed
to a) UV Radiation -Annex F ) |
- |
2200 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
20 |
IS 10889 (2004) |
High density polyethylene films (First Revision) |
-
|
11525 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
5.1(Materials) |
- |
2225 |
|
- |
5.2(Black Compound) |
- |
1625 |
|
- |
6.1.1(Appearance) |
- |
300 |
|
- |
6.1.4(Density) |
- |
500 |
|
- |
6.1.5(Melt Flow Rate) |
- |
1100 |
|
- |
6.1.6(Black Film) |
- |
1625 |
|
- |
6.2.1, Table 1(Nominal Thickness) |
- |
250 |
|
- |
6.2.2, Table 2(Nominal Width) |
- |
250 |
|
- |
6.3, Table 3(Yield Tolerance) |
- |
600 |
|
- |
6.4.1(Tensile Strength at Break) |
- |
2200 |
|
Tensile strength & elongation at break are inclusive |
6.4.2(Elongation at Break) |
- |
0 |
|
- |
6.4.3(Impact Resistance (Falling Dart)) |
- |
850 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
21 |
IS 9755 (2016) |
Textiles – High density polyethylene (HDPE)/ polypropylene (PP) woven sacks for packing fertilizers – Specification (fifth revision) |
-
|
21360 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
3.1(MANUFACTURE-Raw Material- IS 10146 or IS 10910) |
- |
1800 |
|
Linear density & WIDTH & identification all are inclusive |
3.1(MANUFACTURE-Raw Material) |
- |
250 |
|
Visual appearance |
3.2(MANUFACTURE-) |
- |
1500 |
|
- |
3.3(Sacks) |
- |
250 |
|
- |
3.3.1(Sacks-Table 1) |
- |
0 |
|
- |
3.5(Bottom Seam-(see IS 10789).) |
- |
1050 |
|
- |
3.6(Bottom Seam-tThe stitching shall be done
with double fold over seam to a depth of minimum 25 mm, so that the stitches pass through a minimum of six layers of the fabric.) |
- |
500 |
|
- |
3.8(Capacity- The sack shall have the nominal capacity of 50 kg.) |
- |
250 |
|
- |
4.1 , Table 1(REQUIREMENTS) |
- |
5050 |
|
- |
4.2(UV Resistance) |
- |
8260 |
|
- |
4.2(UV Resistance-The HDPE/PP woven fabric of sack made out of UV stabilized material shall have at least 50 percent of the original breaking strength when tested after the
same has been exposed to UV radiation and weathering as per the method given in Annex D.) |
- |
2200 |
|
- |
4.3(Mass-(Annexure E)) |
- |
250 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
22 |
IS 7834 : Part 8 (1987) |
injection moulded PVC socket fittings with solvent cement joints for water supplies: Part 8 Specific requirements for caps |
-
|
1600 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
2.2(Manufacture) |
- |
500 |
|
dimension charge are inclusive |
2.2.2(diameter of the socket of cap) |
- |
0 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
23 |
IS 7834 : Part 7 (1987) |
injection moulded PVC socket fittings with solvent cement joints for water supplies: Part 7 Specific requirements for unions |
-
|
500 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
2.2.2, Table 1(Union Laying
Length) |
- |
500 |
|
All dimensions charges are inclusive |
2.2.3( inside diameter of the socket) |
- |
0 |
|
- |
2.2.3(Socket length) |
- |
0 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
24 |
IS 7834 : Part 6 (1987) |
injection moulded PVC socket fittings with solvent cement joints for water supplies: Part 6 Specific requirements for sockets |
-
|
1600 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
2.2.2, Table 1(Size) |
- |
500 |
|
All dimensions charges are inclusive |
2.2.2, Table 1(Socket Laying
Length) |
- |
0 |
|
- |
2.2.3( inside diameter of the socket) |
- |
0 |
|
- |
2.2.3(Socket length) |
- |
0 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
25 |
IS 7834 : Part 5 (1987) |
Injection Moulded PVC Socket Fittings With Solvent Cement Joints for Water Supplies - Part 5 : Specific Requirements for 45 degree Tees |
-
|
1600 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
2.2.2, Table 1(Size) |
- |
500 |
|
all other dimensions are inclusive to this charge |
2.2.2, Table 1(45 ̊ Tees Laying
Length, Z) |
- |
0 |
|
- |
2.2.2, Table 1(45 ̊ Tees Laying
Length, Z1) |
- |
0 |
|
- |
2.2.3( inside diameter of the socket) |
- |
0 |
|
- |
2.2.3(Socket length) |
- |
0 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
26 |
IS 7834 : Part 4 (1987) |
injection moulded PVC socket fittings with solvent cement joints for water supplies: Part 4 Specific requirements for 90 degree tees |
-
|
1600 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
2.1(General) |
- |
500 |
|
all dimensions charges are inclusive |
2.2.2, Table 1(Size) |
- |
0 |
|
- |
2.2.2, Table 1(90 ̊ Elbow Laying
Length) |
- |
0 |
|
- |
2.2.3( inside diameter of the socket) |
- |
0 |
|
- |
2.2.3(Socket length) |
- |
0 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
27 |
IS 7834 : Part 3 (1987) |
injection moulded PVC socket fittings with solvent cement joints for water supplies: Part 3 Specific requirements for 90 degree elbows |
-
|
4600 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
cl 2.2.2(Dimensions) |
- |
500 |
|
- |
Cl. 2.1 (Ref. Cl. 6.3 of IS 7834 (part 1) : 1987(Effect on water - Lead (first extraction) - Appendix C ) |
- |
3000 |
|
All parameters are included in this charge |
Cl. 2.1 (Ref. Cl. 6.3 of IS 7834 (part 1) : 1987(Effect on water - Lead (third extraction) - Appendix C) |
- |
0 |
|
- |
Cl. 2.1 (Ref. Cl. 6.3 of IS 7834 (part 1) : 1987(Effect on water - Dialkyl tin C4 and higher homologues measured as tin (third extraction) - Appendix C) |
- |
0 |
|
- |
Cl. 2.1 (Ref. Cl. 6.3 of IS 7834 (part 1) : 1987(Effect on water - Other toxic substances (third extraction) - Appendix C) |
- |
0 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
28 |
IS 7834 : Part 2 (1987) |
injection moulded PVC socket fittings with solvent cement joints for water supplies: Part 2 Specific requirements for 45 degrees elbows |
-
|
1600 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
2.2(Manufacture) |
- |
500 |
|
All dimensions charge are inclusive |
2.2.2, Table 1(45 ̊ Elbow Laying
Length) |
- |
0 |
|
- |
2.2.3( inside diameter of the socket) |
- |
0 |
|
- |
2.2.3(socket length) |
- |
0 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
29 |
IS 7834 : Part 1 (1987) |
injection moulded PVC socket fittings with solvent cement joints for water supplies: Part 1 General requirements |
-
|
6725 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
Cl.4(Minimum Thickness) |
- |
500 |
|
- |
Cl. 5.1.1, 5.1.2, Table 1, Fig 1(Minimum Socket Length) |
- |
0.0 |
|
socket length, Internal ID & tolerance all are inclusive in this charge |
Cl. 5.1.1, 5.1.2, Table 1, Fig 1(Mean Socket Internal Diameter at Mid-Point of Socket Length) |
- |
0.0 |
|
- |
Cl. 5.1.1, 5.1.2, Table 1, Fig 1(Out-of-roundness tolerances of socket inside diameter) |
- |
0.0 |
|
- |
Cl. 6.1(Stress Relief Test- Appendix A) |
- |
700 |
|
- |
Cl. 6.2(Opacity- Appendix B) |
- |
575 |
|
- |
Cl. 6.3(Effect on Water[(Lead ( first extraction )]- Appendix C) |
- |
3000 |
|
All effect on water test parameters are included in this charge |
Cl. 6.3(Effect on Water[(Lead ( third extraction )]- Appendix C) |
- |
0 |
|
- |
Cl. 6.3(Effect on Water [Dialkyl tin C4, and higher homologues, measured as tin ( third extraction )]- Appendix C) |
- |
0 |
|
- |
Cl. 6.3(Effect on Water [Other toxic substances ( third extraction )]- Appendix C) |
- |
0 |
|
- |
Cl. 6.4(Short-Term Hydraulic Test- Appendix D) |
- |
850 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |
30 |
IS 6192 (1994) |
Textiles – Monoaxially oriented high density polyethylene tapes – Specification (second revision) |
-
|
4250 View breakup
-
Clause No. |
Exclusion |
Testing Charges (Excl. Of Taxes) |
Effective Date |
Remark |
5.1(Linear density (For test method Refer IS 6193:1971 and IS 7703 Part 1)) |
- |
500 |
|
- |
5.5(Thickness (For test method Refer IS 6193:1971)) |
- |
250 |
|
- |
5.4(Finished width (For test method Refer IS 6193:1971)) |
- |
250 |
|
- |
5.3(Elongation (For test method Refer IS 6193:1971)) |
- |
1100 |
|
- |
5.2(Tenacity (For test method Refer IS 6193:1971)) |
- |
250 |
|
- |
5.6(Heat Shrinkage at 60 degree C(For test method Refer IS 6193:1971)
) |
- |
700 |
|
- |
5.6(Heat Shrinkage at 95 degree C(For test method Refer IS 6193:1971)
) |
- |
700 |
|
- |
4(MATERIAL(Refer IS 7328 :1974)) |
- |
500 |
|
- |
|
Complete
|
|
31 Dec, 2023 |
- |